VICTREX? PEEK POLYMER 150XF

Generic Name: 聚醚醚酮(PEEK) - 提供方: Victrex plc

High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, fine powder for compression moulding, easy flow, FDA food contact compliant, colour natural.

 與典型值比較 - Upgrade to compare!

單位: SI 

總覽
材料狀態(tài)

已商用：當(dāng)前有效

搜索 UL 黃卡

Victrex plc

VICTREX? PEEK POLYMER

供貨地區(qū)

北美洲

非洲和中東

拉丁美洲

歐洲

亞太地區(qū)

機(jī)構(gòu)評(píng)級(jí)

FDA 食品接觸

外觀

自然色

形式

粉狀

加工方法

壓縮模塑

物理性能

額定值

單位制

測(cè)試方法

密度

1.30

g/cm3

ISO 1183表觀密度

0.30

g/cm3

ISO 1183平均顆粒尺寸 - D50

25

μm

ISO 13320-1機(jī)械性能

額定值

單位制

測(cè)試方法

拉伸模量 (23°C)

4100

MPa

ISO 527-1拉伸應(yīng)力 (屈服, 23°C)

100

MPa

ISO 527-2拉伸應(yīng)變 (斷裂, 23°C)

15

%

ISO 527-2彎曲模量 (23°C)

3900

MPa

ISO 178彎曲應(yīng)力 (23°C)

170

MPa

ISO 178沖擊性能

額定值

單位制

測(cè)試方法

懸壁梁缺口沖擊強(qiáng)度 (23°C)

4.5

kJ/m2

ISO 180/A無(wú)缺口伊佐德沖擊強(qiáng)度 (23°C)

無(wú)斷裂

ISO 180熱性能

額定值

單位制

測(cè)試方法

玻璃轉(zhuǎn)化溫度

ISO 11357-2Onset

143

°C

Midpoint

147

°C

熔融溫度

343

°C

ISO 11357-3充模分析

額定值

單位制

測(cè)試方法

熔體粘度 (400°C)

130

Pa·s

ISO 11443補(bǔ)充信息

額定值

單位制

測(cè)試方法

Compression Molding Temperature

380 到 400

°C

Drying Time - Compression molding

3.0 到 5.0

hr

干燥溫度 - Compression molding

120 到 150

°C

注射說明

important notes:

1) Processing conditions quoted in our datasheets are typical of those used in our processing laboratories

Data for mould shrinkage should be used for material comparison. Actual mould shrinkage values are highly dependent on part geometry, mould configuration, and processing conditions.

Mould shrinkage differs for along flow and across flow directions. “Along flow” direction is taken as the direction the molten material is travelling when it exits the gate and enters the mould.

Mould shrinkage is expressed as a percent change in dimension of a specimen in relation to mould dimensions.

2) Data are generated in accordance with prevailing national, international and internal standards, and should be used for material comparison. Actual property values are highly dependent on part geometry, mould configuration and processing conditions. Properties may also differ for along flow and across flow directions.

Detailed data available on our website www.victrex.com or upon request.