基本性能額定值單位測試方法熔體流動速率45g/10minASTM D1238    (190℃/2.16kg)45g/10minISO 1133吸水率 (24 hr)0.2%ASTM D570物理性能額定值單位測試方法比重1.41g/cmASTM D792,ISO 1183成型收縮率    (Flow)1.6-2%ASTM D955,ISO 294-4    (Across Flow)1.6-2%ISO 294-4洛氏硬度ASTM D785    (M-Scale)80    (R-Scale)115機(jī)械性能額定值單位測試方法拉伸模量2900MPaISO 527-2屈服拉伸應(yīng)力67MPaISO 527-2拉伸應(yīng)力61MPaASTM D638斷裂伸長率45%ASTM D63830%ISO 527-2彎曲模量2630MPaASTM D790彎曲強(qiáng)度90MPaASTM D790泰伯耐磨性 (1000 Cycles)14mgASTM D1044CHARPY缺口沖擊強(qiáng)度 (23℃)4.5kJ/mISO 179/1eAIzod 缺口沖強(qiáng)度39J/mASTM D256熱性能額定值單位測試方法熱變形溫度    (0.45MPa,unannealed)158℃ASTM D648    (0.45MPa,unannealed)156℃ISO 75-2/B    (1.8MPa,unannealed)110℃ASTM D648    (1.8MPa,unannealed)105℃ISO 75-2/A流動方向線性熱膨脹系數(shù)0.0001cm/cm/℃ASTM E831阻燃等級HBUL 94